  1. 73m819

    Another way to Bob a Deuce!

    no, Ive tried that, the plating over, the crack still develops under the plate or strong back. i would try HEAVY 3"x3" angle inside the lower frame rail, BOLT not weld, use grade 8 bolts, nuts and oversize HARD washers. this wont help in the heat stress, but will help with twist stress which in...
  2. 73m819

    Another way to Bob a Deuce!

    i beleive you WILL see heat / stress cracks HERE, fron the welding itself combinded with frame twist, just about EVERY frame i have seen welded cracks unless a lot of stress relief , even then most still crack in the long run
108,524members
163,771threads
2,304,077posts
1,217online users
Top
✖
AdBlock Detected

We get it, advertisements are annoying!

Sure, ad-blocking software does a great job at blocking ads, but it also blocks useful features of our website like our supporting vendors. Their ads help keep Steel Soldiers going. Please consider disabling your ad blockers for the site. Thanks!

I've Disabled AdBlock
No Thanks